Effect of chemical surface treatment on topography and retention of glass fiber - reinforced composite posts in primary anterior teeth root canals /
الناشر
Maii Mohamed Mohamed Ahmed Ali ,
المؤلف
Maii Mohamed Mohamed Ahmed Ali
هيئة الاعداد
باحث / Maii Mohamed Mohamed Ahmed Ali
مشرف / Ali Ali Mortada
مشرف / Azza Hashem
مشرف / Dalia Mohamed Moheb
تاريخ النشر
2014
عدد الصفحات
120 Leaves :
اللغة
الإنجليزية
الدرجة
ماجستير
التخصص
Dentistry (miscellaneous)
تاريخ الإجازة
15/4/2015
مكان الإجازة
جامعة القاهرة - الفم والأسنان - Pedodontics
الفهرس
Only 14 pages are availabe for public view

from 144

from 144

Abstract

Several post surface treatments have been recommended to improve the bond strength of resin cements to glass fiber - reinforced composite resin posts in primary teeth root canals. To evaluate the influence of chemical post surface treatment methods on topography and retention of adhesively luted glass fiber - reinforced composite posts in primary teeth. Fifty endodontically treated primary anterior incisors prepared for glass fiber- reinforced composite posts. The posts were submitted to 5 different surface treatments (n = 10): no treatment, silanization, etching with 37% phosphoric, etching with 10% hydrogen peroxide and etching with 21% sodium ethoxide. The posts{u2019} surfaces were examined using an environmental scanning electron microscope (ESEM) then bonded with self - adhesive resin cement (Relay X) and stored in water at 37{u00B0}C for 24 hours.Post retention was measured with push out test at a crosshead speed of 0.5 mm / min using a universal testing machine. Data were analyzed with 1- way ANOVA and the multiple comparisons using