Abstract
The current study evaluated the effect of ultrasonic finishing on marginal accuracy, internal fit and microleakage of empress e-max crowns fabricated by two methods.
In this study, the teeth were divided into two groups according to the type of finish line as the following:
group (c): 20 upper central incisors with a deep chamfer finish line, of a 1mm width.
group (s): 20 upper central incisors with a shoulder finish line, of a 1mm width.
Each group was divided according to the type of finishing tool into two subgroups:
Subgroup (C I): Ten upper central incisors possessing a deep chamfer finish line were finished using low speed conventional finishing stones.
Subgroup (C II): Ten upper central incisors possessing a deep chamfer finish line. The prepared teeth were finished all around using Satelec Perfect Margin chamfer (PM) ultrasonic Kit.
Subgroup (S I): Ten upper central incisors possessing a shoulder finish line were finished using low speed conventional finishing stones.
Subgroup (S II): ten upper central incisors possessing a shoulder finish line were finished all around for each side using a Satelec Perfect Margin Shoulder (PMS) ultrasonic Kit.
The surface roughness was measured at the area of the finish lines of all prepared teeth surfaces to obtain a quantitative comparison of the two finishing protocols by using Stereo microscope.
Electron microscopic scanning was done for evaluation of the morphologic and microstructural changes after finishing.
Forty crowns were constructed using Empress e-max ceramic material using two techniques;
A) CAD/ CAM technique.
B) Heat pressing technique.
The crowns were classified according to manufacture techniques in to two groups:
group (M); manufactured with CAD/ CAM technique.
group (H); manufactured with Heat pressing technique.
Then the forty crowns were placed on their corresponding teeth and held on its place by jig for marginal discrepancy determination before cementation using stereomicroscope.
A measurement of the internal distance before cementation gap was done by using silicon replica technique. Then measurements of microleakage and internal distance were done after cementation by using stereomicroscope.
The results of surface roughness test showed that, the conventional finishing method demonstrated significantly higher roughness values for both finish line preparations (chamfer &shoulder). And the shoulder finish line showed a non-significant increased roughness values in both finishing methods (conventional & ultrasonic).
Results of the vertical marginal accuracy testing before cementation showed that, there was no statistical significant difference between the three groups. The highest mean of vertical gap distance was 71.04 µ for the CAD/CAM crowns with shoulder finish line and finished with conventional stones (GP S I M); while the lowest mean surface roughness value was 46.37 µ for the heat pressed crowns with chamfer finish line and finished with ultrasonic stones (GP C II H).
Results of the vertical marginal accuracy testing after cementation showed that, there was no statistical significant difference between the three groups. The highest mean of internal gap distance was 82.3871 µ for the CAD/CAM crowns with shoulder finish line and finished with conventional stones (GP S I M); while the lowest mean surface roughness value was 49.2380 µ for the heat pressed crowns with chamfer finish line and finished with ultrasonic stones (GP C II H).
Results of internal gap distance before cementation showed there was a statistical significant difference between the three groups. The highest mean internal gap distance was 114.96 µ for the conventionally finished shoulder preparations restored with heat CAD/ CAM crowns (GP SIM), while the lowest mean internal gap distance was 62.38 µ for the conventionally finished chamfer preparations restored with heat pressed crowns (GP CIH).
Results of internal gap distance after cementation showed that; there was a statistical significant difference between the three groups. The highest mean of internal gap distance was 180.3µ for the conventionally finished heat pressed crowns with shoulder finish line (GP S I H), while the lowest mean internal gap distance was 88.79 µ for the ultrasonically finished heat pressed crowns with shoulder finish line (GP S II H).
Results of microleakage showed that; Ultrasonic method showed lower values of microleakage score. There was a statistical significant difference between conventional and ultrasonic finishing regarding microleakage score. Chamfer finish line showed lower values of microleakage score. There was statistically significant difference between chamfer and shoulder finish line regarding microleakage score. There was no statistical significant difference between CAD/CAM and heat pressed techniques regarding microleakage. .ظهرت افكار عديده لتطوير طريقة تحضير الاءسنان لاءستقبال التيجان. واحده من ضمن احدث الاختراعات فى هذا المجال هى استخدام جهاز الموجات فوق صوتيه. اول استخدام للموجات فوق الصوتيه كان لكحت الجير ثم تطور ليستخدم فى علاج الجذور ثم فى حشو الاسنان والان استخدم فى تحضير الاءسنان. يمتاز جهاز الموجات فوق صوتيه باءن له ذبذبه خاصه بخلاف الطريقه العاديه تؤدى الى زيادة دقة الحواف وعدم احداث اى ضرر للثه والعصب والاسنان المجاوره. كل هذه المزايا تؤدى الى سهولة و دقه المقاس بعد التحضير و الى زيادة التصاق التاج بحافة السنه مما يؤدى الى عدم حدوث تسوس بعد اللصق.
اهداف الدراسه:
الهدف من هذه الدراسه هو تقيييم تاثير استخدام جهاز الموجات فوق صوتيه على خشونة أسطح الاءسنان و الانطباق الحافى و الداخلى و مقاومة التسرب لتيجان الخزف ثنائى السليكات المصنعه بطريقتين مختلفتين بأستخدام نوعين من خط الانهاء .
الطرق و المواد المستخدمه:
استخدمت اربعون سنه اماميه فوقيه مخلوعه للتحضير الكامل وهذه الاسنان تقسم الى مجموعتين طبقا لنوع الة التحضير.
المجموعه الاولى: عشرون سنه اماميه فوقيه مخلوعه حضرت بواسطة استخدام جهازالسى ان سى وقد انهي التحضير باستخدام الموجات فوق صوتيه.
المجموعه الثانيه: عشرون سنه اماميه فوقيه مخلوعه حضرت بواسطة استخدام جهازالسى ان سى وقد انهي التحضير باستخدام موتور التحضير العادى ذى السرعه العاليه.
وهذه المجموعتين قسمت داخليا الى مجموعتين طبقا لشكل الحافه :
المجموعه (أ) : حافه قائمة الجوانب.
المجموعه (ب) : حافه حافه مستديرة الجوانب.
وقد استخدمت تيجان الخزف ثنائى السليكات مصنعه بطريقتين:
الطريقه الاولى: بالكاد كام
الطريقه الثانيه: بالضغط الحرارى
و قد وضع كل طربوش على التحضير المخصص له ثم تم مسكهم باحكلم عن طريق جهاز (جج) وذلك لقياس دقة انطباق الحواف قبل اللصق باستخدام الاستريوميكروسكوب ايضا قيست بواستطه خشونة كل حافة.
تم قياس المسافة الداخلية بين الطربوش والسنة المحضرة قبل اللصق وذلك باستنساخ هذه المسافة بواسطة المطاط ثم قياس سمك هذا المطاط تحت الاستريوميكروسكوب.
تم لصق هذه العينات وقيست دقة انطباق الحواف بعد اللصق باستخدام الاستريوميكروسكوب ثم تعرضت هذه العينات لاختلاف درجات الحرارة من البارد (5 درجة مئوية) الى الساخن (55 درجة مئوية) ثم تكررت هذه الدورات الحرارية حوالى 50 الف لفة ثم نقعت فى محلول الميثلين بلو لمدة 24 ساعة فى درجة حرارة الغرفة ثم قطعت العينات باستخدام المنشار الى نصفين حيث قيست درجة التسرب وسمك اللصق باستخدام الاستريوميكروسكوب.
اثبتت النتائج الاتى :
1 – العينات المحضرة باستخدام موتور التحضير العادى ذى السرعة العالية هى اكثر خشونة من الموجات وان الحافة القائمة هى اكثر خشونة من الحافة المستديرة.
2 - اثبت اختبار دقة الحواف قبل اللصق انه لا يوجد اختلاف بين العينات.
3 - اما بعد اللصق فقد كانت العينات المحضرة بواسطة الموجات وتملك حافة مستديرة ومغطاه بطربوش ومصنع بالضغط الحرارى حازت على افضل انطباق بين الطربوش والتحضير.
4 - اما العينات المحضرة بواسطة الموتور العدى ذى السرعة العالية وتملك حافة مستقيمة ومغطاة بطربوش مصنع بالكاد كام هى اقل المجموعات فى درجة الانطباق بين الطربوش وحافة التحضير.
5 – اما اختبار التسرب وايضا اختبار قياس سمك اللصق فقد اثبتوا ان افضل المجموعات انطباقا داخليا واقلهم تسربا هى العينات المحضرة بواسطة الموجات فوق الصوتية وتملك حافة مستديرة ومغطاه بطربوش مصنع بالضغط الحرارى اما اقل المجموعات انطباقا دخليا واكثرهم تسربا هى العينات المتحضرة بالتحضير العادى ولها حافة مستقيمة ومغطاه بالطربوش المصنع بالكاد كام.
لذلك فقد اثبتت هذه الدراسة نجاح انهاء التحضير بواسطة الموجات فى دقة الانطباق الحافى والداخلى ومقاومة التسرب.
ان التيجان اوالطرابيش المصنعة بواسطة الضغط هى افضل من المصنعة بواسطة الكاد كام وان الحافة المستديرة هى افضل من القائمة من حيث دقة الانطباق الحافى والداخلى ومقاومة التسرب.
,